Two layer mirror for LCD-on -silicon products and method of fabrication thereof

ABSTRACT

A method of fabricating an LCD-on-silicon pixel device, comprising the following steps. A substrate having an upper layer of silicon is provided. A via is formed in the silicon layer. An opaque conducting layer is deposited over the silicon layer, filling the via. The opaque conducting layer is planarized a reflective layer is deposited over the opaque conducting layer. Alternatively, the via may be formed by a deposition and etch back process with one metal. An opaque conducting layer is then deposited and planarized before deposition of the reflective layer. An LCD-on-silicon pixel device, comprises a substrate having an upper silicon layer. The upper silicon layer has a plug therein comprised of an opaque conducting material. Over the upper silicon layer and the opaque conducting plug is a planar opaque conducting layer and a planar reflective layer is over the planar opaque conducting layer.

FIELD OF THE INVENTION

[0001] The present invention relates generally to LCD-on-silicon devices, and specifically to a method of fabricating two layer mirror LCD-on-silicon pixels.

BACKGROUND OF THE INVENTION

[0002] The top metal layer of a LCD-on-silicon display pixel serves both as a mirror to reflect light and as an electrode to control the gray scale of the top LCD material. Aluminum (Al) is normally used because of its high reflectivity and its compatibility to integrated circuit production. If the aluminum layer is thick (>2000 Å), then the grain size is normally big which degrades reflectivity. If the aluminum layer is thin (<2000 Å), then light penetrates through the aluminum layer and affects the functioning of the transistor below by the photoelectric effect. Also, the via, which serves as the electrical connection to the top metal pixels, usually produces a dimple on the aluminum layer which also affects reflectivity.

[0003] U.S. Pat. No. 5,486,485 to Kim et al. describes a method of forming a plurality of SOI (silicon-on-insulator) transistors in a pattern beneath planarized reflective surfaces of a reflective display.

[0004] U.S. Pat. No. 5,946,547 to Kim et al. describes a method of fabricating LCD devices using three patterning steps. When reflective-type LCD devices are fabricated, a reflective layer comprised of Al, for example, may be formed on the rear surface of the substrate opposite the patterned conductive layer to prevent loss of light which penetrates through the pixel electrode.

[0005] U.S. Pat. No. 5,633,182 to Miyawaki et al. describes a method of manufacturing an image display device wherein the switching (driving) transistor and the interconnection layer are formed on one of the surfaces of the insulating layer (insulator) which is remote from the liquid crystal layer while the liquid crystal voltage applying electrode is formed on the other surface of the insulating layer close to the liquid crystal layer. Thus it is possible to provide a light-blocking layer near the transistor allowing the aperture ratio to be increased, reducing the cross-talk among the adjacent pixels, and increasing the S/N ratio.

[0006] U.S. Pat. No. 5,471,330 to Sarma describes a liquid crystal display pixel and a method of forming same, wherein each pixel has a thin film transistor with a silicon pixel electrode. A doping and recrystallization of the silicon is effected to increase the electrical conductivity and light transmittance of the silicon adequately for the pixel electrode. An ITO (indium tin oxide) layer is not required for the pixel electrode.

SUMMARY OF THE INVENTION

[0007] Accordingly, it is an object of the present invention to provide LCD-on-silicon pixels and a method of fabricating LCD-on-silicon pixels using a thin aluminum layer.

[0008] Another object of the present invention is to provide LCD-on-silicon pixels and a method of fabricating LCD-on-silicon pixels having a planar upper surface unaffected by any defects in the underlying via.

[0009] A further object of the present invention is to provide LCD-on-silicon pixels and a method of fabricating LCD-on-silicon pixels with increased reflectivity of the aluminum mirror by depositing a thin aluminum layer with small grain.

[0010] Yet another object of the present invention is to provide LCD-on-silicon pixels and a method of fabricating LCD-on-silicon pixels that prevent light penetrating the aluminum mirror layer and affecting the underlying transistor junctions by photoelectric effect.

[0011] Another object of the present invention is to provide LCD-on-silicon pixels and a method of fabricating LCD-on-silicon pixels that permit an increase in the permissible amount of light to fall on the pixels so as to have a larger and/or clearer overall picture/images.

[0012] Other objects will appear hereinafter.

[0013] It has now been discovered that the above and other objects of the present invention may be accomplished in the following manner. Specifically, a substrate having an upper layer of silicon is provided. A via is formed in the silicon layer. An opaque conducting layer is deposited over the silicon layer, filling the via. The opaque conducting layer is planarized and a reflective layer is deposited over the opaque conducting layer to form an LCD-on-silicon pixel device. Alternatively, the via may be formed by a deposition and etch back process with one metal. An opaque conducting layer is then deposited and planarized before deposition of the reflective layer. An LCD-on-silicon pixel device, comprises a substrate having an upper silicon layer. The upper silicon layer has a plug therein comprised of an opaque conducting material. Over the upper silicon layer and the opaque conducting plug is a planar opaque conducting layer and a planar reflective layer is over the planar opaque conducting layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] The features and advantages of the two layer mirrors for LCD-on-silicon devices, and the method of fabricating same, according to the present invention will be more clearly understood from the following description taken in conjunction with the accompanying drawings in which like reference numerals designate similar or corresponding elements, regions and portions and in which:

[0015] FIGS. 1 schematically illustrates in cross-sectional representation a method of forming an LCD-on-silicon mirror element known to the inventors.

[0016]FIGS. 2 through 6 schematically illustrate in cross-sectional representation a preferred embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0017] Unless otherwise specified, all structures, layers, etc. may be formed or accomplished by conventional methods known in the prior art.

[0018] Process Known to the Inventors

[0019]FIG. 1 illustrates a method of forming an LCD-on-silicon mirror element known to the inventors. Vias 202 are formed within an upper layer of silicon oxide (SiO₂) on substrate 200. Vias 202 have depressions or dimples 204 in their upper surface resulting from the formation of vias 202.

[0020] Dimples 204 are transferred to overlying barrier metal layers 206 formed over substrate 200 and vias 202 as barrier layer dimples 208.

[0021] Aluminum layers 210 formed over barrier layers 206 similarly have barrier layer dimples 208 transferred as aluminum layer dimples 212.

[0022] Optical interface layers 214 formed over the exposed sides and upper surfaces of aluminum layers again similarly have aluminum layer dimples 212 transferred as optical interface layer dimples 216.

[0023] It is desired that all light rays reflect off the upper surface of the LCDon-silicon mirror elements. However, in this LCD-on-silicon mirror element design, if aluminum layers 210 are thin, i.e. less than about 2000 Å, then light rays designated “A” penetrate aluminum layers 210. Further, if aluminum layers 210 are thick, i.e. greater than about 2000 Å, then light rays designated “B” scatter because of the larger aluminum grain size. Additionally, aluminum layer dimples 212 affect reflectivity due to their concave structure.

PREFERRED EMBODIMENT OF THE PRESENT INVENTION

[0024] Accordingly as shown in FIGS. 2-5, fabrication of a pair of LCD-on-silicon two layer mirror pixels are illustrated. Of course only one such pixel, or more than two pixels may be fabricated in according with the present invention.

[0025]FIG. 2 shows a cross sectional view of an inter-metal dielectric layer 6 and interconnects 8. The inter metal dielectric layer 6 and interconnects overlie a substrate having devices (such as field effect transistor (FETS) and conductive lines interconnecting the devices).

[0026] As shown in FIG. 2, an intermetal dielectric (IMD) layer 11 is etched to form via openings 12.

[0027] Barrier layer 14 is formed over the surface of the inter metal dielectric (IMD) layer 11 and covers the sidewalls of the via openings 12. Barrier layer 14 is preferably a metal layer comprised of titanium/titanium nitride (Ti/TiN) and may also be comprised of cobalt nitride. Metal barrier layer has a thickness of from about 200 to 2000 Å, and more preferably from about 600 to 1000 Å.

[0028] Opaque conducting layer (e.g., intermediate conductive layer) 16 is then formed over substrate 10, filling barrier metal lined vias 12. Conducting layer 16 is an intermediate conductive layer that is hard enough to be processed by chemical mechanical polishing (CMP), or other planarizing processes, and is also dense enough to stop light from penetrating therethrough. Opaque conducting layer 16 is deposited from about 5000 to 30,000 Å above the surface of the IMD layer 11, and more preferably from about 8000 to 15,000 Å above the surface of the IMD layer 11.

[0029] Conducting layer 16 may be comprised of tungsten (W), titanium (Ti), titanium nitride (TiN), chromium (Cr), silver (Ag), cobalt, or cobalt nitride and is preferably tungsten. Conducting layer 16 is not comprised of Al.

[0030] Opaque conducting layer 16 may be a single material deposited in one step, as shown in FIG. 2. Alternately, as shown in FIG. 6, the opaque conducting layer be comprised of a lower plug 15 and a upper opaque conducting layer 16 a 16B. The lower plug 15 and the opaque conducting layer can be formed of the same material or two different materials. A first layer fills barrier lined vias 12 to form the plugs 15. Then we deposit in a second layer to blanket cover intermetal dielectric layer and the plug to the above noted thickness over inter metal dielectric layer 11.

[0031] In either event, intermediate conducting layer 16 includes dimples 18 that are transferred from dimples (not shown) formed over vias 12 by the process of filling vias 12.

[0032] As shown in FIG. 3, in an important step in the present invention, conducting layer 16 is polished back and planarized, preferably by chemical mechanical polishing, to remove dimples 18 and to form an optically flat upper surface 20 preferably to a thickness of from about 500 to 2000 Å.

[0033] A thin reflective layer 22 is then deposited over optically flat upper surface 20 of conducting layer 16 to a thickness of from about 300 to 2000 Å, and more preferably from about 1000 to 2000 Å. Reflective layer 22 may be comprised of aluminum (Al), an aluminum copper alloy (AlCu), or aluminum silicon copper alloy (AlSiCu) and is preferably Al.

[0034] If is noted that the upper surface 24 of reflective layer 22 maintains the optical flatness of upper surface 20 of conducting layer 16.

[0035] As shown in FIG. 4, the device is patterned to define the top metal layer, i.e. reflective layer 22 and conducting layer 16, as separate mirror pixels 26 a, 26 b with like portions 14 a, 14 b; 16 a, 16 b; 20 a, 20 b; 22 a, 22 b; 24 a, 24 b; respectively. For example, a photoresist layer (not shown) may be deposited and patterned with the subsequent etching of the device at 30. The photoresist layer is then stripped and removed.

[0036] As shown in FIG. 5, optical interface layers 28 may then be deposited to enhance the reflected light and to passivate the exposed mirror surfaces 24 a, 24 b; 32 a, 32 b. Optical interface layers 28 may be comprised of ON (i.e., an oxide layer over a nitride layer), ONON, ONONON, etc., up to five (5) ON pairs, or other multiple transparent coatings that enhance light reflection. This completes formation of the two layer mirror LCD-on-silicon products of the present invention.

[0037] While particular embodiments of the present invention have been illustrated and described, it is not intended to limit the invention, except as defined by the following claims. 

We claim:
 1. A method of fabricating a LCD-on-silicon pixel device, comprising the steps of: providing a substrate having an upper layer of silicon; forming a via in said silicon layer; depositing an opaque conducting layer over said silicon layer, filling said via; planarizing said opaque conducting layer; and depositing a reflective layer over said opaque conducting layer.
 2. The method of claim 1, wherein said opaque conducting layer is selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride.
 3. The method of claim 1, wherein said reflective layer is selected from the group comprising aluminum, an aluminum copper alloy, and an aluminum silicon copper alloy.
 4. The method of claim 1, wherein said planarized opaque conducting layer is from about 500 to 5000 Å thick.
 5. The method of claim 1, wherein said planarized opaque conducting layer is from about 500 to 2000 Å thick.
 6. The method of claim 1, wherein said opaque conducting layer is planarized by chemical mechanical polishing.
 7. The method of claim 1, wherein said reflective layer is from about 300 to 2000 Å thick.
 8. The method of claim 1, wherein said reflective layer is from about 1000 to 2000 Å thick.
 9. The method of claim 1, wherein said reflective layer is comprised of aluminum and is from about 300 to 2000 Å thick.
 10. The method of claim 1, wherein said reflective layer is comprised of aluminum and is from about 1000 to 2000 Å thick.
 11. The method of claim 1, including the step of forming a barrier layer over said silicon layer and lining said via before said opaque conducting layer deposition.
 12. The method of claim 1, including the step of forming optical interface layers over said reflective layer.
 13. The method of claim 1, including the step of forming optical interface layers over said reflective layer; said optical interface layers being selected from the group comprising ON and multiple layers of ON.
 14. A method of fabricating an LCD-on-silicon pixel device, comprising the steps of: providing a substrate having an upper layer of silicon; forming a via in said silicon layer; forming a plug within said via comprised of a first opaque conducting layer; depositing a second opaque conducting layer over said silicon layer and said first opaque conducting layer plug; planarizing said opaque conducting layer; and depositing a reflective layer over said opaque conducting layer.
 15. The method of claim 14, wherein said first opaque conducting layer is selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride, and said second opaque conducting layer is different from said first opaque conducting layer and is selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride.
 16. The method of claim 14, wherein said reflective layer is selected from the group comprising aluminum, an aluminum copper alloy, and an aluminum silicon copper alloy.
 17. The method of claim 14, wherein said planarized second opaque conducting layer is from about 500 to 5000 Å thick.
 18. The method of claim 14, wherein said planarized second opaque conducting layer is from about 500 to 2000 Å thick.
 19. The method of claim 14, wherein said second opaque conducting layer is planarized by chemical mechanical polishing.
 20. The method of claim 14, wherein said reflective layer is from about 300 to 2000 Å thick.
 21. The method of claim 14, wherein said reflective layer is from about 1000 to 2000 Å thick.
 22. The method of claim 14, wherein said reflective layer is comprised of aluminum and is from about 300 to 2000 Å thick.
 23. The method of claim 14, wherein said reflective layer is comprised of aluminum and is from about 1000 to 2000 Å thick.
 24. The method of claim 14, including the step of forming a barrier layer over said silicon layer and lining said via before said first opaque conducting layer deposition.
 25. The method of claim 14, wherein said first and second opaque conducting layers are comprised of the same material.
 26. The method of claim 14, including the step of forming optical interface layers over said reflective layer.
 27. The method of claim 14, including the step of forming optical interface layers over said reflective layer; said optical interface layers being selected from the group comprising ON and multiple layers of ON.
 28. An LCD-on-silicon pixel device, comprising: a substrate having an upper silicon layer; a plug within said upper silicon layer; said plug comprised of an opaque conducting material; a planar opaque conducting layer over said upper silicon layer and said opaque conducting plug; and a planar reflective layer over said planar opaque conducting layer.
 29. The device of claim 28, wherein said opaque conducting plug is selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride, and said planar opaque conducting layer is comprised of a material different from said opaque conducting plug and is comprised of a material selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride.
 30. The pixel device of claim 28, wherein said opaque conducting plug and said planar opaque conducting layer are integral and are comprised of a material is selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride, and selected from the group comprising tungsten, titanium, titanium nitride, chromium, silver, cobalt, and cobalt nitride.
 31. The device of claim 28, wherein said reflective layer is selected from the group comprising aluminum, an aluminum copper alloy, and an aluminum silicon copper alloy.
 32. The device of claim 28, wherein said planar opaque conducting layer is from about 500 to 5000 Å thick.
 33. The device of claim 28, wherein said planar opaque conducting layer is from about 500 to 2000 Å thick.
 34. The device of claim 28, wherein said planar opaque conducting layer is planarized by chemical mechanical polishing.
 35. The device of claim 28, wherein said reflective layer is from about 300 to 2000 Å thick.
 36. The device of claim 28, wherein said reflective layer is from about 1000 to 2000 Å thick.
 37. The device of claim 28, wherein said reflective layer is comprised of aluminum and is from about 300 to 2000 Å thick.
 38. The device of claim 28, wherein said reflective layer is comprised of aluminum and is from about 1000 to 2000 Å thick.
 39. The device of claim 28, including a barrier layer over said silicon layer and lining said via.
 40. The device of claim 28, including optical interface layers over said reflective layer.
 41. The device of claim 28, including optical interface layers over said reflective layer; said optical interface layers being selected from the group comprising ON and multiple layers of ON. 